Hastelloy C2000 Alloy Bar
Hastelloy C2000 bars (UNS N06200 / W.Nr 2.4675) are a nickel-chromium-molybdenum alloy with copper as the alloying element. It can be considered an improved version of alloy C-22, exhibiting superior corrosion resistance in both reducing and oxidizing environments. This alloy is ductile, easy to weld, and possesses excellent resistance to pitting corrosion, crevice corrosion, and stress corrosion cracking, making it one of the most widely used alloys in chemical processing.
Chemical Composition
|
Element |
Content (%) |
|
Nickel, Ni |
59 |
|
Chromium, Cr |
23 |
|
Molybdenum, Mo |
16 |
|
Copper, Cu |
1.6 |
|
Silicon, Si |
0.080 |
|
Carbon, C |
0.010 |
Physical Properties
|
Properties |
Metric |
Imperial |
|
Density |
8.50 g/cm³ |
0.307 lb/in³ |
Mechanical Properties
|
Properties |
Metric |
Imperial |
|
Tensile strength (@ thickness 25.4 mm/ 1.00 in.) |
752 MPa |
109000 psi |
|
Yield strength (@ 20°C/ 68°F, thickness 12.7 mm/0.5000 in, 0.2% offset) |
345 MPa |
50000 psi |
|
Elongation at break (@ thickness 6.35 mm/0.250 in., in 50.8 mm) |
62% |
62% |
Application
Hastelloy C2000 alloy bar can be used in applications requiring high metallurgical stability in reducing or oxidizing atmosphere. It is also used in chemical process equipment applications.
Chemical processing plant components - reactors, heat exchangers, valves, pumps - for both reducing and oxidizing environments.
Hot Tags: hastelloy c2000 alloy bar, China hastelloy C2000 alloy bar manufacturers, UNS N06200,ASTM B574,NiCr23Mo16Cu,Ni-Cr-Mo-Cu Alloy,hastelloy C2000 alloy Rod & Bar,Forged bar